Reef Tank Disaster- Need Help
Hi everyone,
So I came home Christmas Day to my 250g reef tank shattered, everything everywhere, everything dead. Really brutal. I'm trying to figure out what happened, the guy who built the tank is blaming the guy who built the stand and vise versa. Pictures are below. Any thoughts or ideas on how to figure out what happened? Tank is about 6 months old. 1 inch acrylic. thank so much! Nick |
01/02/2017, 01:45 PM | #2 |
Registered Member
Join Date: Jan 2015
Posts: 547
|
Wow im sorry thats messed up! the level on the third pic is a little off ? the only thing i can thinknof it wasnt level and it caused the the tank to twist and cause pressure and breaking it . Hope your house is ok after that
Sent from my iPhone using Tapatalk |
01/02/2017, 08:58 PM | #3 |
Registered Member
Join Date: Jul 2016
Location: Oakdale, MN
Posts: 461
|
Ouch! Sorry about the loss of the tank and the mess in the house. I hope it all works out for you in the end.
|
01/03/2017, 06:07 AM | #4 |
Registered Member
Join Date: Jan 2017
Posts: 2
|
Thanks everyone! Getting cleaned up slowly!
|
01/03/2017, 10:17 AM | #5 |
Registered Member
Join Date: Mar 2016
Location: Portland, OR
Posts: 2,032
|
Was there solid contact all around between the tank bottom and the plywood? If there was a slight gap, it could've put a lot of extra stress in that corner.
__________________
Brian Current Tank Info: 110 gallon |
01/03/2017, 10:29 AM | #6 |
Grizzled & Cynical
Join Date: Apr 2006
Location: Stamford, CT
Posts: 17,319
|
Merry Christmas
That really stinks. Would have thought 1" acrylic almost bulletproof at that size.
__________________
Simon Got back into the hobby ..... planned to keep it simple ..... yeah, right ..... clearly I need a new plan! Pet peeve: anemones host clowns; clowns do not host anemones! Current Tank Info: 450 Reef; 120 refugium; 60 Frag Tank, 30 Introduction tank; multiple QTs |
01/03/2017, 10:31 AM | #7 |
Registered Member
Join Date: Apr 2011
Location: San Diego, CA
Posts: 1,405
|
Did you use some foam under the tank between the wood and acrylic? Not sure if thats required with acrylic but I use it for my glass tank to help even out the stress.
__________________
180G Rimless Starphire 72x24x24 (Miracles) 3 x Ecotech XR15w G4 Pro | T5 x 4 | 2 x Mp40wQD GEO 612 Cal Reactor | Vertex Omega 150 Skimmer | Chaeto Reactor Synergy Reef CL44 Sump | Neptune Apex |
01/03/2017, 10:37 AM | #8 |
Registered Member
Join Date: Sep 2013
Location: Louisville Kentucky
Posts: 3,110
|
Loooking at picture 3 tells the story..
To me from bonding acrylic that area looks like it was not bonded well it likely let loose causing stress on the Acrylic then there was likely a burr at the top where it let loose at.. Other thing i cant tell. I see that the level shows its out but still inside the level.. How much out depends on how long your level is compared to how long the stand is.. If that is a 6 foot tank and a 5 ft level thats prob 1/8th out.. if that is a 6 foot tank and a 2 ft level you are closer to 1/2 to 5/8th out.... If you do not have a long level use a Piece of hose as a water level . be sure to cross check from back left corner to front right corner... a acrylic tank will shift enough to not pop a seam like that if its only out a bit. but if its Twisted its stressed all over... Just my thoughts on how i would check to determine what went wrong.... Remember the floor could have also sagged over time......
__________________
240+G Mixed BB Reef tank.. 350 G Marine Pond. And the expensive stuff that runs it. Chic's are for Chic's You silly men Go Fishing or something... Current Tank Info: 240= gal Reef /550 Gallon Saltwater pond 72 G Bay front Tropical aquarium |
01/03/2017, 10:37 AM | #9 | |
Registered Member
Join Date: Sep 2013
Location: Louisville Kentucky
Posts: 3,110
|
Quote:
__________________
240+G Mixed BB Reef tank.. 350 G Marine Pond. And the expensive stuff that runs it. Chic's are for Chic's You silly men Go Fishing or something... Current Tank Info: 240= gal Reef /550 Gallon Saltwater pond 72 G Bay front Tropical aquarium |
|
01/03/2017, 10:42 AM | #10 |
Registered Member
Join Date: Jan 2014
Location: Oklahoma
Posts: 348
|
The only thing that bothers me about this is the clean seperation at the corner. I was under the impression that when properly glued the two pieces actually welded together. I wouldn't expect to see a clean seperation at a seam in that case. With that being said, I am not a structural engineer or an expert on acrylic construction so take that observation for what it's worth.
|
01/05/2017, 07:23 AM | #11 |
Registered Member
Join Date: Oct 2015
Posts: 59
|
I'd personally say it was a badly bonded edge that caused that, as if it's bonded correctly the sheet itself would fail before the bond and that's a complete seperation from that edge.
|
01/05/2017, 09:24 AM | #12 |
Registered Member
Join Date: Jan 2015
Posts: 1,598
|
This is a living nightmare. Unfortunately, it doesn't matter what anybody thinks the cause is, the tank builder is going to stick with his gun and deny any warranty. This is the game they always play; blame it on something else.
__________________
325G DT. 100G sump. In-sump refugium. SRO-5000SSS. 2 Gyres 150. 2 Water Blaster HY-5000. 2 Razor 320W. Apex Gold. MR2 GFO. 2 800W Heaters. Tunze Osmolater. 2 20g-long QT tanks. Geo 624 CA. 80W UV |
01/05/2017, 10:41 AM | #13 | |
Registered Member
Join Date: Apr 2011
Location: San Diego, CA
Posts: 1,405
|
Quote:
I would definitely go after the tank builder.
__________________
180G Rimless Starphire 72x24x24 (Miracles) 3 x Ecotech XR15w G4 Pro | T5 x 4 | 2 x Mp40wQD GEO 612 Cal Reactor | Vertex Omega 150 Skimmer | Chaeto Reactor Synergy Reef CL44 Sump | Neptune Apex |
|
01/05/2017, 10:46 AM | #14 |
Registered Member
Join Date: Jun 2009
Location: Winnipeg
Posts: 141
|
This was specifically due to the build of the tank. This will be lengthy, but I find it's far better to have your brain loaded before you shoot your mouth off, so this will help load up your ammo bags before calling the tank builder.
He's hoping you're naive or ignorant. I built my own Drop off reef tank, and have been welding acrylic for years as it's just another substrate used in the signage industry. Number 1 - Material used. When doing tanks, any supplier of the plastic who is worth their weight will suggest ONLY cast acrylic made in the USA. It's stronger and better than the Chinese counterparts. I'm in Canada, so either is imported for me...however American cast acrylic is more expensive, so many builders quietly choose other sources or use extruded acrylic. http://www.pmma.dk/acryl_stobt_kontr...spx?Lang=en-GB Number 2 - What is welding acrylic? Well, they call it "welding" when in reality it's not really a weld. I prefer to call it "melding" http://wikidiff.com/meld/weld Melding - To combine two similar objects into one. (cue "when 2 become 1" from Spice Girls lol ) Basically you have different levels of "weldon" it starts with very watery thin, all the way up to 2 part weldon. The type of "Weldon" you use is dependent on the thickness of acrylic used and the stress it's required to hold. Usually you use pins lying on their sides and place the properly sanded smooth acrylic edge directly where you want it, sitting on top of the pins...You then inject the weldon (thin as water) using the provided applicator. This draws the weldon into the seam using capillary action. The pins are there simply to provide a gap between the 2 locations the "Meld" will take place. This is necessary as the weldon creates a chemical reaction with the acrylic and melts it on both places as the capillary action actually holds the weldon only where the join will be. You generally wait 1-2 minutes and then slowly remove the pins and allow the edge to slowly touch down onto the other side after the pins are all pulled out. The other option is using a thicker Weld-on like 16 or 40 and applying it like a glue, you leave a quarter inch extra on the edge of the panel, lay down the other edge and let the thick Weld-On squeeze out like silicon on the extra quarter inch part...Let it cure and then come back with a router and trim the quarter inch peice w/ the extra squished out weld-on off. This is how the professional builders on TV do it. Once it's polished up it's perfect. These 2 pieces should be one piece of plastic now. One properly made acrylic tank is technically just one piece of plastic when finished. It does not have seams or "welds" 1" thick acrylic should not crack or explode as shown, it should also be capable of twisting or bending slightly, so as long as the stand isn't obviously out of wack. This assuming the builder used quality acrylic. What is possible is when he was building it, instead of the tried and true method of routering the edge, razoring it, and sanding/polishing to a fine finish prior to melding the acrylic together, he used a heat source (torch) and this caused crazing during the weldon process. If any crazing occured this would create the ideal conditions to eventually fail with a crack like fracture. We generally do not have ovens available for annealing edges with acrylic properly, and a quick fix is to use a torch, however any professional plastics company (who I deal with weekly) only uses oxy-propane or oxy-acetylene torchs to polish acrylic edges, as normal torches can actually create crazing, which I've had the luxury of doing to my own projects. lol This is all just subjective as I have no idea how your builder built the tank. That being said, when building an acrylic tank there are numerous variables involved: 1- Acrylic material used - extruded is lower quality and more prone to manufacturer defects. You want American made cast acrylic for ANY large aquarium. The problem is the vast majority of customers have no idea about the acrylic, where it comes from, or how it's made so this is a simple way for builders to save on costs. (not saying he did, but it's common place) 2- Was all the acrylic the exact same brand & type? Did he use cast for the bottom and extruded for the sides? Did he use off cuts or farm it from older sheets he had from previous projects? The Weld-On may not work as expected when used with different types together. 3- What type of Weld-On was used? 3,4,16,40? Did he use it properly? Was it the watery thin fast set? Was it the 2 part? Some Weld-On solvents suggest surface annealing prior to bonding to prevent crazing. Below is the link for Weld-on, click on each type and the material data sheet to see the bonding strength. http://www.eplastics.com/plexiglass_glue 4- Were the joints properly cleaned and smooth prior to the bond? How did he smooth out the edges which were bonded? Was a router used? Scrapers? Torch to save time? 5- Were clamps used to hold it in place? Was the solvent squeezed out? How much contact time with the solvent to soften the acrylic prior to bonding? The stand on the other hand is a simple beast. All it does is hold something up. Whether the tank is level is irrelevant with 1" thick acrylic. As long as something isn't rocking the tank back and forth causing undue twisting/stress the stand has nothing to do with it. Acrylic has the ability to withstand bending far better than glass. If his immediate response is to blame the stand builder, you should be very cautious about that. It means he's ran into this before and immediately jumps to a scapegoat instead of solving the problem for you. Any professional builder, when running into a situation like this should have your best interests in mind. Let's fix the problem instead of ponder about it and work together accomplishing that. Not spread blame. Basically, if the tank was built properly, the break should never have happened where the meld occured. In simple terms - they gave you a faulty tank. Either the meld wasn't done correctly or crazing happened during production. The second photo shows exactly what happened. This is the top of the tank, where the water line is not touching so a leak will not be visible, however the weight is always present across the whole panel. At the end of the day if their is an improper meld or lack thereof, where the meld is correct is where the break occurred and there is a shard of acrylic still attached. Meaning there wasn't enough solvent applied, it got squished out during clamping, or they didn't allow enough contact time for the chemical reaction to take place prior to the bond...OR the edges were not smooth/clean enough for bonding. This would explain why it would hold water and eventually fail. It's like weighing down 5 feet of a 4' x 8' sheet of plywood, as I walk out eventually it will break and it will break exactly at the first place it's firmly weighted down at. Stick to your guns, the home run here is a 1" thick acrylic tank for only 250 gallons is overkill, and there is no excuse for it to fail where it's supposed to be chemically "welded" together whether its the meld itself or crazing from the meld, it's his fault. Write down a check list, call the builder, and go through it, asking very specific questions. What type of acrylic did you use? Extruded or Cast? How did you prep the edges prior to bonding? What type of Weld-On did you use? Do you clamp the pieces together after the bond or use a jig to hold it in place? Is it possible during the bonding process the edges were not prepped properly? What process do you use to smooth the edges prior to bonding? Router? Razor by hand? Torch? How long do you allow the Weld-On to soften the acrylic prior to bond? Is it possible not enough solvent was applied? Is it possible it may have been clamped too hard resulting in the solvent being squished out? Why is there a clean break where it's supposed to be welded? Isn't where the acrylic is chemically bonded supposed to be far stronger than the panes? Hope this helps! Be professional and polite and do it in person if possible. If not, then do it over the phone as email is well.....email. Oh and when discussing the meld....make sure you call it a "weld" even though that's an incorrect term. It's a chemical reaction joining them into one piece, not something holding them together tightly. I guess the solvent is called "weld-on" so people have learned to call it a weld. Either way, they call it a "weld" in the industry, like they pronounce the football player "Favre" Farv. It's wrong but it's just the way it is. lol |
01/05/2017, 11:18 AM | #15 |
Cheesy Poofs!
Join Date: May 2014
Location: Bronx, New York
Posts: 357
|
That would be my worst nightmare... Sorry for the loss.
__________________
Ecotech Radion XR15 Pro Gen3 x2, ReefLink, CPR CS50 Overflow. Reef Octopus NWB 110 Skimmer, Reef Octopus BR-110 Reactor. VorTech MP40 w/ QD Wetside x2, MP10 x1(Sump), 30-Gallon Sump. Current Tank Info: 60 Gallon, Prepping for LPS, 6 Years. |
01/06/2017, 05:46 PM | #16 |
Registered Member
Join Date: Aug 2012
Posts: 275
|
Not an expert, but if I were to make some speculations here is what it would be:
- Out of level. Even a bit on a tank this big can cause a good amount of stress. - No foam that I can see under the tank - nowhere for it to go (sag) to "level" itself. Combined with the out of level, quite a bit of twisting stress could have had no where to go but into the joint. - Potentially an imperfect seam, but I think under normal circumstances it probably would have held given the thickness.
__________________
Terence Fugazzi :: VP Sales and Marketing :: Neptune Systems Come on over and check out the Neptune Systems Community Forum for the latest tricks, tips, and support help with your Apex AquaController. http://forum.neptunesystems.com |
01/08/2017, 08:38 AM | #17 |
Registered Member
Join Date: Jun 2016
Location: Earth
Posts: 88
|
That level makes it look like the back panel would pop if it was just a stress thing eh?
|
01/08/2017, 09:35 AM | #18 | ||
Registered Member
Join Date: Sep 2013
Location: Louisville Kentucky
Posts: 3,110
|
Quote:
Quote:
I am no Expert by any means with Acrylic .But i have bonded a lot of it not just for tanks over the years.. Take two pieces of acrylic say even 1/4 inch.. Bond them using the proper method. let them sit over night.. Try and Break the bond apart.. YOU WILL Crack the acrylic at its weakest point if it breaks where it was bonded it will pull chunks out of both pieces not rip out the seam.. ACRYLIC Tanks can take a lot of twisting this is one of the reasons they are better for larger tanks. Of course the down side is they scratch so easily.. As said above by a EXPERT... Acrylic when bonded properly becomes 1 piece of acrylic... the seam should NEVER BREAK CLEANLY IF PROPERLY BONDED.. Sorry keep
__________________
240+G Mixed BB Reef tank.. 350 G Marine Pond. And the expensive stuff that runs it. Chic's are for Chic's You silly men Go Fishing or something... Current Tank Info: 240= gal Reef /550 Gallon Saltwater pond 72 G Bay front Tropical aquarium |
||
01/08/2017, 11:56 AM | #19 |
Registered Member
Join Date: Jul 2010
Location: Wooster, OH
Posts: 1,862
|
Looks like an improper weld to me, but like many others, I'm no expert.
__________________
60x36x24 mixed reef. 40b sump. Regal 250int Varios. 4xHydra26HDs+t5s. 4xMp40wes. Apex2016. |
01/09/2017, 05:21 AM | #20 |
Registered Member
Join Date: Sep 2014
Posts: 705
|
That seam is way too clean to be anything other than a bad solvent weld.
|
01/10/2017, 11:39 PM | #21 | |
Registered Member
Join Date: Jan 2017
Posts: 8
|
Quote:
|
|
01/11/2017, 01:28 AM | #22 |
Registered Member
Join Date: Mar 2016
Location: New Brunswick Canada
Posts: 627
|
Great post by mickey204 above. I would ask those same questions.
Last resort: If you determine that its the tank's construction, you could always pull a "Trump" and threaten him with legal action... not only for the cost of the tank, but its contents and any subsequent damage and clean-up costs to the house. My lawyer will write up just about any letter for $100...they usually don't care if you have a case or not. That only matters if it goes to court (which you would have no intention of doing) This is a last resort of course, and if he calls your bluff, you are out the $100...but you would be surprised about the attitude change that can take place when someone is threatened with a lawyer's letter to sue. Have the lawyer put in something about working out a compromise with you personally, with a deadline, to avoid any further action. I would be mad as h3ll if this had happened to me through no fault of my own. I appreciate your frustration. |
02/01/2017, 11:43 AM | #23 |
Registered Member
Join Date: Dec 2014
Location: Indiana
Posts: 56
|
Sorry about your tank Nortner. Thanks Mickey for taking the time to document the process. Very interesting and informative.
|
02/05/2017, 09:01 AM | #24 |
Moved on
Join Date: Apr 2000
Location: Coastal Texas
Posts: 16,000
|
What a Christmas present.
I think mickey204 seem to know best. Follow his reason suplement with your own research and try to get some recourse. IME, the stand level or not is not all that important. It is weather or not it is in a flat plane and weather or not it have enough support, though out the bottom and side for acrylic. 1 inch acrylic 250 gal tank is way overkill and should not fail. It is a bad tank.
__________________
Minh My homepage is my album here at Reef Central Current Tank Info: Reboot 320 anemones reef. Angels: Yellow Chest Regal(2), Flame (2). Copperband But. Tangs: Yellow, Purple. Wrasse: about 20 wrasses various species. Anemones: Giantea X4 (Breen, Blue, Purple and Multicolors), Haddoni X1 Red, Magnifica X1 Purpletip |
|
|